Compositions containing ethylene-based polymer and cycloolefin interpolymer, and films formed from the same

ABSTRACT

A composition comprising at least the following components: A) an ethylene-based polymer; B) a cycloolefin inter-polymer comprising, in polymerized form, ethylene and at least one bridged cyclic olefin selected from Structures a-d, as described herein, or any combination of Structures a-d; and wherein component A is present in an amount ≥50 wt %, based on the weight of the composition, and wherein component B is present in an amount from 5 to 12 wt %, based on the sum weight of components A and B.

REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No. 62/549,147, filed Aug. 23, 2017.

BACKGROUND

There is a need for compositions that can be used to form films that can be used to form wrap or bags, and which do not need to be stripped off from the enclosed material (for example, polymer pellets) during the mixing of the enclosed material. As a result, the film gets incorporated and dispersed during the mixing process. The films should also possess enough stiffness and heat seal strength for proper use in industrial scale bagging lines.

Polymer compositions and/or films are described in the following references: WO2003097355, WO2011129869, WO2015004311, WO2008137285, EP1525092A1, EP3016865A1, EP2744648A1, EP717759A1, US2006005741, US20140308466, US20140363600, US20140170742, US20140170379, US20150336652, US20150282978, US20160303833, US20160136934, US20160244229, U.S. Pat. Nos. 4,918,133, 6,090,888, 6,984,442, 7,288,316, 8,663,810, 9,050,243, 9,452,593, CN104943309A (abstract), KR2000057382A (abstract), CA2269672A, CA2410483C, CA2170042A1 and JP2001505610A (abstract). However, as discussed above, there remains a need for compositions to be used in films that have good stiffness and flowability, and can be used for wrap or bags that do not need to be stripped off from the enclosed material, when mixing the enclosed material. These needs have been met by the following invention.

SUMMARY OF INVENTION

A composition comprising at least the following components:

-   A) an ethylene-based polymer; -   B) a cycloolefin interpolymer comprising, in polymerized form,     ethylene and at least one bridged cyclic olefin selected from the     following:     -   a)

Structure a, wherein R1 and R2 are each, independently, selected from hydrogen, an alkyl;

-   -   b)

Structure b, wherein R3 and R4 are each, independently, selected from hydrogen, an alkyl;

-   -   c)

Structure c, wherein R5 and R6 are each, independently, selected from hydrogen, an alkyl;

-   -   d)

Structure d, wherein R7 and R8 are each, independently, selected from hydrogen, an alkyl;

-   -   e) or any combination of a) through d); and

wherein component A is present in an amount ≥50 wt %, based on the weight of the composition, and wherein component B is present in an amount from 5 to 12 wt %, based on the sum weight of components A and B.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows DSC profiles for an EVA, a POE, and a high stiffness polymer (COC) with material transitions in the range from 70° C. to 100° C.

FIG. 2 depicts the “V0.1 (melt viscosity) versus wt % COC” profiles for the noted compositions.

FIG. 3 is a bar graph depicting the V0.1 values for the noted compositions.

FIG. 4 depicts the “Ec versus Tc (peak)” profiles for the noted polymers and compositions.

FIG. 5 depicts the “E1 versus Tm” profiles for the noted examples.

FIG. 6 depicts the “E2 versus Tc onset at end of melting” profiles for the noted examples.

DETAILED RESCRIPTION

Compositions have been discovered that can be used to form films that have an optimal balance of melting temperature, stiffness and seal strength. Such films can be used to form wrap or bags for polymer materials, such as EPDM pellets, and such films do not need to be stripped off from the enclosed polymer. Such films have low melting temperatures, and are incorporated and dispersed during the mixing process of the enclosed polymer. These films also possess enough stiffness and heat seal strength for proper use in industrial scale bagging lines.

As discussed above, a composition is provided, comprising at least the following components:

-   A) an ethylene-based polymer; -   B) a cycloolefin interpolymer comprising, in polymerized form,     ethylene and at least one bridged cyclic olefin selected from the     following:     -   a)

Structure a, wherein R1 and R2 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic), further R1 and R2 are each, independently, selected from hydrogen or a C1-C6 alkyl, or hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen;

-   b)

Structure b, wherein R3 and R4 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic), further R3 and R4 are each, independently, selected from hydrogen or a C1-C6 alkyl, or hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen;

-   c)

Structure c, wherein R5 and R6 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic), further R5 and R6 are each, independently, selected from hydrogen or a C1-C6 alkyl, or hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen;

-   -   d)

Structure d, wherein R7 and R8 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic), further R7 and R8 are each, independently, selected from hydrogen or a C1-C6 alkyl, or hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen;

-   -   e) or any combination of a) through d); and

wherein component A is present in an amount ≥50 wt %, based on the weight of the composition, and wherein component B is present in an amount from 5 to 12 wt %, based on the sum weight of components A and B.

The composition may comprise a combination of two or more embodiments described herein. Each component of the composition may comprise a combination of two or more embodiments described herein.

In one embodiment, the cycloolefin interpolymer of component B has a Tg from 60° C. to 90° C., or from 65° C. to 90° C.

In one embodiment, the ethylene-based polymer of component A has a Tm from 70° C. to 95° C., or from 85° C. to 90° C.

In one embodiment, the ethylene-based polymer of component A has a density ≤0.900 g/cc, or ≤0.890 g/cc, or ≤0.885 g/cc, or ≤0.880 g/cc (1 cc=1 cm³).

In one embodiment, the ratio of the Tg of component B to the Tg of component A is from −1.0 to −5.0, or from −1.1 to −4.5, or from −1.1 to −4.0, or from −1.1 to −3.5, or from −1.1 to −3.0, or from −1.1 to −2.5.

In one embodiment, component B is present in an amount from 5 to 12 wt %, or from 5 to 11 wt %, or from 5 to 10 wt %, based on the sum weight of components A and B.

In one embodiment, component B is present in an amount from 5 to 12 wt %, or from 5 to 11 wt %, or from 5 to 10 wt %, based on the weight of the composition.

In one embodiment, the weight ratio of component A to component B is from 4.0 to 20.0, or from 5.0 to 20.0, or from 5.0 to 15.0, or from 7.0 to 11.0, or from 8.0 to 10.0.

In one embodiment, the ethylene-based polymer of component A is an ethylene/alpha-olefin interpolymer, or an ethylene/alpha-olefin copolymer, or an ethylene/C3-C8 α-olefin copolymer.

In one embodiment, the ethylene-based polymer of component A is an ethylene/alpha-olefin/diene interpolymer, and further an ethylene/propylene/diene terpolymer (EPDM). In a further embodiment, the diene is ENB.

In one embodiment, the ethylene-based polymer of component A is an ethylene-vinyl acetate (EVA) copolymer.

In one embodiment, component A is present in an amount ≥55 wt %, or ≥60 wt %, or ≥65 wt %, or ≥70 wt %, or ≥75 wt %, or ≥80 wt %, or ≥85 wt %, or ≥84 wt % based on the weight of the composition. In one embodiment, component A is present in an amount ≤95 wt %, or ≤94 wt %, or ≤93 wt %, or ≤92 wt %, or ≤91 wt %, or ≤90 wt %, based on the weight of the composition.

In one embodiment, the composition comprises ≥80 wt %, or ≥85 wt %, or ≥90 wt %, or ≥95 wt %, or ≥98 wt % of the sum of component A and component B, based on the weight of the composition. In one embodiment, the composition comprises ≤100 wt %, or ≤99 wt % of the sum of component A and component B, based on the weight of the composition.

In one embodiment, the composition comprises less than 1.0 wt %, or less than 0.5 wt % of a polymer comprising, in polymerized form, styrene, and optionally, one or more other comonomers.

In one embodiment, the cycloolefin interpolymer is an ethylene/bridged cyclic olefin copolymer.

In one embodiment, the at least one bridged cyclic olefin selected from the following:

-   -   a)

Structure a, wherein R1 and R2 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic). In a further embodiment, R1 and R2 are each, independently, selected from hydrogen or a C1-C6 alkyl, and further hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen.

In one embodiment, the at least one bridged cyclic olefin selected from the following:

-   -   b)

Structure b, wherein R3 and R4 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic). In a further embodiment, R1 and R2 are each, independently, selected from hydrogen or a C1-C6 alkyl, and further hydrogen or a C1-C5 alkyl, or hydrogen or a C 1-C4 alkyl, or hydrogen or a C 1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen.

In one embodiment, the at least one bridged cyclic olefin selected from the following:

-   -   c)

Structure c, wherein R5 and R6 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic). In a further embodiment, R1 and R2 are each, independently, selected from hydrogen or a C1-C6 alkyl, and further hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen.

In one embodiment, the at least one bridged cyclic olefin selected from the following:

-   -   d)

Structure d, wherein R7 and R8 are each, independently, selected from hydrogen, an alkyl (linear or branched or cyclic). In a further embodiment, R1 and R2 are each, independently, selected from hydrogen or a C1-C6 alkyl, and further hydrogen or a C1-C5 alkyl, or hydrogen or a C1-C4 alkyl, or hydrogen or a C1-C3 alkyl, or hydrogen or a C1-C2 alkyl, or hydrogen or methyl, or hydrogen.

In one embodiment, the cycloolefin interpolymer of component B comprises, in polymerized form, ethylene and only one bridged cyclic olefin selected from Structures a to d as defined herein.

In one embodiment, the composition further comprises an ethylene vinyl acetate copolymer. In a further embodiment, the ethylene vinyl acetate copolymer is present in an amount from 5 to 20 wt %, based on the weight of the composition.

In one embodiment, the composition does not contain a coupling agent, for example, an azide compound or a peroxide.

The composition may comprise one or more additional additives. Suitable additives include, but are not limited to, fillers, antioxidants, UV stabilizers, flame retardants, colorants or pigments, crosslinking agents, slip agents, antiblocks, and combinations thereof. In one embodiment, the composition comprises one or more additional additives in an amount from 0.5 to 20 wt %, or 1 to 15 wt %, or 5 to 10 wt %, based on the weight of the composition. In a further embodiment, the composition comprises a slip agent and/or an antiblock in an amount from 0.5 to 20 wt %, or 1 to 15 wt %, or 5 to 10 wt %, based on the weight of the composition.

In one embodiment, the composition further comprises a thermoplastic polymer. Such polymers include, but are not limited to, propylene-based polymers, ethylene-base polymers, and olefin multi-block interpolymers. Suitable ethylene-base polymers include, but are not limited to, high density polyethylene (HDPE), linear low density polyethylene (LLDPE), low density polyethylene (LDPE), homogeneously branched linear ethylene/α-olefin interpolymers or copolymers, and homogeneously branched substantially linear ethylene/α-olefin interpolymers or copolymers (that is homogeneously branched long chain branched ethylene/α-olefin interpolymers or copolymers).

In one embodiment, the composition has a Tm ≥80° C., or ≥81° C., or ≥82° C. In one embodiment, the composition has a Tm ≤90° C., or ≤88° C., or ≤86° C.

In one embodiment, the composition has a V0.1 (190° C.) value ≥35,000 Pa·s, or ≥40,000 Pa·s, or ≥45,000 Pa·s. In one embodiment, the composition has a V0.1 (190° C.) value ≤65,000 Pa·s, or ≤60,000 Pa·s, or ≤55,000 Pa·s.

In one embodiment, the composition has a V100 (190° C.) value from 2,800 Pa·s to 4,000 Pa·s, or from 3,000 Pa·s to 3,800 Pa·s, or from 3,200 Pa·s to 3,600 Pa·s.

In one embodiment, the composition has a V0.1/V100 (RR) value ≥10, or ≥11, or ≥12. In one embodiment, the composition has a V0.1/V100 (RR) value ≤16, or ≤15, or ≤14.

In one embodiment, the composition has an E1 value from 0.84 to 0.92, or from 0.85 to 0.91, or from 0.86 to 0.90.

In one embodiment, the composition has an E2 value from 0.92 to 0.98, or from 0.93 to 0.97, or from 0.94 to 0.96.

In one embodiment, the composition has an Ec value from 0.40 to 0.60, or from 0.41 to 0.59, or from 0.42 to 0.58.

Also is provided a film comprising at least one layer formed from the composition of any one or more embodiments described herein. In a further embodiment, the film comprising a core layer formed from a core composition comprising ≤1.0 wt %, or ≤0.5 wt %, or ≤0.2 wt %, ≤0.1 wt % of an ethylene/bridged cyclic olefin interpolymer or copolymer. In a further embodiment, the core composition does not comprise an ethylene/bridged cyclic olefin interpolymer or copolymer.

In one embodiment, the film comprises at least one additional layer, formed from a composition comprising from 1 to 12 wt % of an ethylene/bridged cyclic olefin interpolymer or copolymer, based on the weight of this composition.

Also is provided a film comprising at least three layers a/b/c, and wherein layer b is formed from a composition comprising ≤1.0 wt %, or ≤0.5 wt %, or ≤0.2 wt %, ≤0.1 wt %, or none, of an ethylene/bridged cyclic olefin interpolymer or copolymer; and wherein the layer a and/or layer c are each, independently, formed from a composition of one or more embodiments described herein.

Also is provided a film comprising at least five layers a/b/c/d/e, and wherein layer c is formed from a composition comprising ≤1.0 wt %, or ≤0.5 wt %, or ≤0.2 wt %, ≤0.1 wt %, or none, of an ethylene/bridged cyclic olefin interpolymer or copolymer; and wherein the layer a, layer b, layer d and/or layer e are each, independently, formed from a composition of one or more embodiments described herein.

Also is provided a film comprising at least six layers a/b/c/d/e/f, and wherein layer c and layer d are each, independently, formed from a composition comprising ≤1.0 wt %, or ≤0.5 wt %, or ≤0.2 wt %, ≤0.1 wt %, or none, of an ethylene/bridged cyclic olefin interpolymer or copolymer; and wherein the layer a, layer b, layer e and/or layer f are each, independently, formed from a composition of one or more embodiments described herein.

In one embodiment, a film comprising at least one layer formed from the composition of any one or more embodiments described herein has a thickness of from 0.5 to 10 mil, or from 4 to 7 mil, or from 5 to 6 mil.

Also is provided an article comprising at least one component formed from the composition of any one or more embodiments described herein.

Also is provided an article comprising at least one component formed from the film of any one or more embodiments described herein.

Definitions

Unless stated to the contrary, implicit from the context, or customary in the art, all parts and percents are based on weight, and all test methods are current as of the filing date of this disclosure.

The term “composition,” as used herein, includes the material(s), which comprise the composition, as well as reaction products and decomposition products formed from the materials of the composition. Any reaction product or decomposition product is typically present in trace or residual amounts.

The term “polymer,” as used herein, refers to a polymeric compound prepared by polymerizing monomers, whether of the same or a different type. The generic term polymer thus embraces the term homopolymer (employed to refer to polymers prepared from only one type of monomer, with the understanding that trace amounts of impurities can be incorporated into the polymer structure) and the term interpolymer as defined hereinafter. Trace amounts of impurities, such as catalyst residues, can be incorporated into and/or within the polymer.

The term “interpolymer,” as used herein, refers to polymers prepared by the polymerization of at least two different types of monomers. The term interpolymer thus includes the term copolymer (employed to refer to polymers prepared from two different types of monomers) and polymers prepared from more than two different types of monomers.

The term, “olefin-based polymer,” as used herein, refers to a polymer that comprises, in polymerized form, 50 wt % or a majority amount of olefin monomer, for example ethylene or propylene (based on the weight of the polymer), and optionally may comprise one or more comonomers.

The term “ethylene-based polymer,” as used herein, refers to a polymer that comprises, in polymerized form, 50 wt % or a majority weight percent of ethylene (based on the weight of the polymer), and optionally may comprise one or more comonomers.

The term “ethylene-based interpolymer,” as used herein, refers to an interpolymer that comprises, in polymerized form, a 50 wt % or a majority weight percent of ethylene (based on the weight of the interpolymer), and at least one comonomer.

The term, “ethylene-based copolymer,” as used herein, refers to a copolymer that comprises, in polymerized form, 50 wt % or a majority amount of ethylene monomer (based on the weight of the copolymer), and an α-olefin, as the only two monomer types.

The term, “ethylene/α-olefin copolymer,” as used herein, refers to a copolymer that comprises, in polymerized form, 50 wt % or a majority amount of ethylene monomer (based on the weight of the copolymer), and an α-olefin, as the only two monomer types.

The term, “propylene-based polymer,” as used herein, refers to a polymer that comprises, in polymerized form, a majority amount of propylene monomer (based on the weight of the polymer), and optionally may comprise one or more comonomers.

The terms “comprising,” “including,” “having,” and their derivatives, are not intended to exclude the presence of any additional component, step or procedure, whether or not the same is specifically disclosed. In order to avoid any doubt, all compositions claimed through use of the term “comprising” may include any additional additive, adjuvant, or compound, whether polymeric or otherwise, unless stated to the contrary. In contrast, the term, “consisting essentially of” excludes from the scope of any succeeding recitation any other component, step or procedure, excepting those that are not essential to operability. The term “consisting of” excludes any component, step or procedure not specifically delineated or listed.

As one of ordinary skill in the art would understand, the term “COC” refers to a cyclic olefin copolymer.

Test Methods Differential Scanning Calorimetry (DSC) (Component A, Component B, Composition)

Differential Scanning Calorimetry (DSC) is used to measure melting and crystallization behavior of polymers (e.g., ethylene-based (PE) polymers). In the case of compounded Bland, the sample is first melt pressed (25000 lbs for about 10 sec) into a thin film, at about 175° C., and then cooled to room temperature. About 5 to 8 mg of polymer film sample is cut with a die punch and is weighed and placed into a DSC pan. In the case of fabricated films, the sample is directly punched from the film. The lid is crimped on the pan to ensure a closed atmosphere. The sample pan is placed into a calibrated DSC cell purged with nitrogen gas, and then heated at a rate of approximately 10° C./min, to a temperature of 180° C. The sample is kept at this temperature for three minutes. Then the sample is cooled at a rate of 10° C./min to −40° C. to record the crystallization trace, and kept isothermally at that temperature for three minutes. The sample is next reheated at a rate of 10° C./min, until complete melting. Unless otherwise stated, peak melting point (Tm) is determined from the first heating curve, and corresponds to the temperature of the highest peak (intensity) in the endotherm. The crystallization temperature (Tc) is determined from the cooling curve (peak Tc). The onset end of the melting temperature can be defined as the extrapolated end of the melting curve calculated from the intersection of two lines a and b, where a is the tangent with the point of maximum slope on the secondary side of the peak and b is the extrapolation of the baseline after the melting. The Tg is measured from the second heating curve, and determined at the midpoint of the inflection transition. Some DSCs transitions are shown in FIG. 1.

Tensile Strength and Tensile Energy to Break (MD and CD)

Tensile Strength and Tensile Energy to Break (MD and CD) were measured in accordance with ASTM D882-10 (average of five film samples in each direction; each sample “1 in×6 in” or 25 mm×150 mm). Before characterization samples were preconditioned for 40 hours at temperature from 21° C. to 25° C., and relative humidity of 50%±5. Preparation of each film is described in the experimental section below.

Density

Samples that are measured for density are prepared according to ASTM D-1928. Within one hour of sample pressing, measurement are made using ASTM D-792, Method B.

Melt Index

Melt index (I₂) is measured in accordance with ASTM-D 1238, Condition 190° C./2.16 kg, and is reported in grams eluted per 10 minutes.

Dynamic Mechanical Spectroscopy (DMS)

Small angle oscillatory shear (melt DMS) was performed using a TA Instruments ARES, equipped with “25 mm parallel plates,” under a nitrogen purge. The time between sample loading, and the beginning of the test, was set to five minutes for all samples. The experiments were performed at 120° C., over a frequency range of 0.1 to 100 rad/s. The strain amplitude was adjusted, based upon the response of the samples, from 1 to 10%. The stress response was analyzed in terms of amplitude and phase, from which, the storage modulus (G′), loss modulus (G″), dynamic viscosity η*, tan delta, and phase angle were determined. The viscosities V0.1 at 190° C. and V100 at 190° C., and rheology ratio (V0.1/V100 at 190° C.; also referred to as “RR”) were recorded. Specimens for Dynamic Mechanical Spectroscopy were “25 mm diameter×3.3 mm thick” compression molded discs, formed at 180° C., and 10 MPa molding pressure, for five minutes, and then quenched between chilled platens (15-20° C.) for two minutes.

EXPERIMENTAL

The following examples illustrate the present invention but are not intended to limit the scope of the invention. Materials are listed below. Polymers are typically stabilized with ppm amounts of one or more stabilizers.

ELVAX® 460 (hereinafter “ELVAX 460”) is an EVA, available from DuPont, with a density of 0.941 g/cc (1 cc=1 cm³), a melt index (I2) of 2.5 g/10 min, and a VA content of 18 wt % (based on the weight of the EVA).

ELVAX® 470 (hereinafter “ELVAX 470”) is an EVA, available from DuPont, with a density of 0.94 g/cc, a melt index (I2) of 0.7 g/10 min, and a VA content of 18 wt % (based on the weight of the EVA).

AMPACET 100329 is a slip agent, available from AMPACET Corp.

AMPACET 100342 is an antiblock, available from AMPACET Corp.

AMPACET 10090 is a slip agent, available from AMPACET Corp.

AMPACET 100450 is an antiblock, available from AMPACET Corp.

ALCUDIA® PA-539 (hereinafter “ALCUDIA 539”) is an EVA, available from Entec Polymers, with a density of 0.937 g/cc, a melt index (I2) of 2 g/10 min, and a VA content of 18 wt % (based on the weight of the EVA).

ALCUDIA® PA-537 (hereinafter “ALCUDIA 537”) is an EVA, available from Entec Polymers, with a density of 0.941 g/cc, a melt index (I2) of 0.7 g/10 min, and a VA content of 18 wt % (based on the weight of the EVA).

ENGAGE™ 8003 (hereinafter “ENGAGE 8003”) is an ethylene/octene copolymer, available from The Dow Chemical Company, with a density of 0.885 g/cc, a melt index (I2) of 1.0 g/10 min and a Tg of −46° C.

ENGAGE™ 8540 (hereinafter “ENGAGE 8540”) is an ethylene/octene copolymer, available from The Dow Chemical Company, with a density of 0.908 g/cc, a melt index (I2) of 1.0 g/10 min, and a Tg of -32° C.

ENGAGE™ 8100 (hereinafter “ENGAGE 8100”) is an ethylene/octene copolymer, available from The Dow Chemical Company, with a density of 0.87 g/cc, a melt index (I2) of 1.0 g/10 min and a Tg of −52° C.

NORDEL™ IP 4820 (hereinafter “NIP4820”) an EPDM, available from The Dow Chemical Company, with a density of 0.88 g/cc, a melt index (I2) of 1.0 g/10 min and a Tg of −18° C.

AFFINITY™ PF 1140G POP (hereinafter “AFFINITY 1140”) is an ethylene/octene copolymer (random), available from The Dow Chemical Company, with a density of 0.897 g/cc, a melt index (I2) of 1.6 g/10 min, and a Tg of −33° C.

AFFINITY™ VP 8770G1 POP (hereinafter “AFFINITY 8770”) is an ethylene/octene copolymer (random), available from The Dow Chemical Company, with a density of 0.885 g/cc, a melt index (I2) of 1.0 g/10 min, and a Tg of −46° C.

VERSIFY™ 2200 (hereinafter “VERSIFY 2200”) is an propylene/ethylene copolymer, available from The Dow Chemical Company, with a density of 0.876 g/cc, and a melt flow rate at 230° C. (MFR) of 2.0 g/10 min.

LDPE 132I is polyethylene homopolymer available from The Dow Chemical Company, with a density of 0.921 g/cc, and a melt index (I2) of 0.25 g/10 min.

TOPAS® 9506F-04 (hereinafter “TOPAS 9506F-04”) is a COC copolymer (ethylene and norbornene), available from Topas Advanced Polymers, with a density of 1.02 g/cc, a melt volume rate (MVR), at 230° C./2.16 kg (ISO 1133), of 6 cm³/10 min, a melt index, at 190° C./2.16 kg, of 0.9 g/10 min, and a Tg of 63° C.

TOPAS® 8007F-04 (hereinafter “TOPAS 8007F-04”) is a COC copolymer (ethylene and norbornene), available from Topas Advanced Polymers, with a density of 1.02 g/cc, a melt volume rate (MVR), at 230° C./2.16 kg (ISO 1133), of 12 cm³/10 min, a melt index, at 190° C./2.16 kg, of 1.8 g/10 min, and a Tg of 77° C.

“AB” refers to 20 wt % of Talc AB compounded with 80 wt % ENGAGE 8003.

Properties of Compositions Rheology

To determine the melt-flow properties of polymers and the above polymer compositions, dynamic oscillatory shear measurements were conducted over a range from 0.1 rad s⁻¹ to 100 rad s⁻¹, at a temperature of 120° C. and 10% strain, using stainless steel, parallel plates of “25-mm diameter.” See above DMS test method. Test sample has 25 mm diameter and a thickness of 3.3 mm, on a strain-controlled rheometer, ARES/ARES-G2 by TA Instruments. The V0.1 and V100 are the viscosities at 0.1 rad s⁻¹ and 100 rad s⁻¹, respectively, with V0.1/V100 ratio being a measure of shear thinning characteristics. The effect of the “COC” content on the composition rheology are shown below in Tables 1-3. See also FIG. 2 and FIG. 3.

TABLE 1 ENGAGE 8003 ENGAGE 8003 ENGAGE 8003 ENGAGE 90 wt %:TOPAS 70 wt %:TOPAS 50 wt %:TOPAS 8003 8007F-04 8007F-04 8007F-04 TOPAS (EO-03) 10 wt % 30 wt % 50 wt % 8007F-04 wt % TOPAS 0 10 30 50 100 V0.1 (190° C.), Pa · s 40,693 46,221 68,946 106,810 512,117 V100 (190° C.), Pa · s 3,334 3,443 3,756 4,092 5,900 RR (V0.1/V100) 12 13 18 26 87 % Increase in V0.1 14 69 162 1158 vs EO-03

TABLE 2 ENGAGE 8003 ENGAGE 8003 90 wt %: TOPAS (EO-03) TOPAS 9506F-04 10 wt % 9506F-04 wt % TOPAS added to EO-03 0 10 100 V0.1 (190° C.), Pa · s 40,693 46,112 372,615 V100 (190° C.), Pa · s 3,334 3,440 5,582 RR (V0.1/V100) 12 13 67 % Increase in V0.1 vs EO-03 13 816

TABLE 3 Effect of 10% COC on the V0.1 of various POEs (1 MI, 0.908-0.870 density) at 130° C. ENGAGE ENGAGE ENGAGE ENGAGE ENGAGE ENGAGE 8540 8003 8100 8540 8003 8100 90 wt 90 wt 90 wt 90 wt 90 wt 9 0wt %:TOPAS %:TOPAS %:TOPAS %:TOPAS %:TOPAS %:TOPAS ENGAGE ENGAGE ENGAGE 8007F-04 8007F-04 8007F-04 9506F-04 9506F-04 9506F-04 8540 8003 8100 10 wt % 10 wt % 10 wt % 10 wt % 10 wt % 10 wt % 46,531 40,693 39,396 51,976 46,221 44,753 51,627 46,112 44,589 Pa · s Pa · s Pa · s Pa · s Pa · s Pa · s Pa · s Pa · s Pa · s

Film Production

Inventive (Inv.) and comparative (Comp.) films are presented below. Tables 7A-7F and 8 show the compositions of each layer of each film; each weight percent is based on total weight of the respective composition used to form each film layer. Each composition used to form each film layer was prepared using a HAAKE Rheomix 3000, equipped with roller mixing blades, at a mixing speed of 40 RPM. The raw materials were dry mixed before adding to the mixer, which was preheated to 150° C. A mixing time of five minutes was used after the addition of raw materials and the securing of the ram.

Each five layer film (skin/intermediate/core/intermediate/skin) was produced on a five-layer blown film line. The blown film line was a 75 mm 5-Layer Flat Die (30/10/20/10/30), with 25 mm skin extruders and 20 mm intermediate/core extruders. The line had a Dual Lip Air Ring, ABS Gravimetric Feed, and Dual Surface Winders. Films from 0.8 mils to 6 mils thickness can be produced, with blow up ratios from 2.2 to 3.9, production rates from 9 to 27 kg/hr, and haul-off from 2.4 to 18 meter per min. The line was capable of on-line slitting and separating film layers. On-line slitting and separating film layers were performed for all examples except for Inv. F4. On-line slitting and film layer separation was not performed in Inv. F4, but instead left as a collapsed bubble. Table 6 below provides the processing conditions for the production of multilayer (5) films.

Inv. F3 and Comp. F12 were prepared on a seven layer blown film line. The remaining films were prepared on the five layer blown film line. The Alpine 7-Layer Coextrusion Blown Film Line was used to fabricate Inv. F3 and Comp. F12. This line consisted of a 7-layer coex die with inserts available in widths of 200 mm and 250 mm, a 7-50 mm 30:1 L/D grooved fed extruders utilizing barrier type screws, four component Maguire in-line blenders for each extruder, ExVis an Alpine control system, an NDC gauge thickness detection system with auto gauging, a 358° oscillating nip roll capable of speeds up to 400 fpm and film width of 60 inches, and a Pillar corona device. Table 8 below shows the compositions for each film layer and film process conditions for the production of each seven layer film. Each weight percent is based on total weight of the respective composition used to form each film layer. See also Table 9. Some additional film properties are shown in Tables 10A-10C below.

Tensile Properties

Tensile properties will be defined by the modulus of the compositions of the films. The higher the modulus, the higher the stress the composition can handle, without significant deformation. The information here reported the stress required to deform the composition 7% and 25% in the machine direction (MD). See Table 5 below.

Processing Time

Here the processing time is the time required for the compositions of the films to cool down below the transition temperature of the composition therefore recovering the typical properties of a solid-like composition. It is known that the higher the transition temperature, the faster the composition sets. It has been discovered that a temperature dependent constraint of 60° C., above which crystallization should have already taken place, was suitable for the inventive compositions. To describe the crystallization profile above this temperature, the parameter Ec was defined as the fraction of the enthalpy of crystallization above 60° C., relative to the total enthalpy of crystallization measured by DSC. The FIG. 4 shows “Ec as a function of the crystallization temperature peak (TC peak)” for four sets of compositions described below. See Tables 4 and 5 below.

A set of “18 wt %VA EVAs” with a peak melting temperature of 88° C. These compositions show a relatively high Tc and Ec values, indicating that more than 40% of the enthalpy of crystallization occurred well above the 60° C. constraint. An Ec of 0.4 (40%) is expected to result in acceptable processing times.

Ethylene-based polymers with melting temperatures from 75° C. to 95° C. An increase in crystallinity drives both Tc and Ec upwards (increase in Tc and Ec). This set of samples meets the Ec of 0.4. The POEs exhibiting Tm lower than 75° C., have a Tc value lower than the 60° C. constraint (Ec approaching to zero, i.e., ENGAGE 8100, 0.87 density, 1 MI), and their processing would be excessively long.

Compositions of propylene based elastomers (PBE) with POE's. Typically a PBE will have a higher modulus than a POE, and this higher modulus will increase the modulus of PBE/POE blend to that approaching EVA. However, the PBE fraction in the blend crystallizes well below the “60° C. temperature constraint,” therefore affecting the EC of the blend, and making its processing unpractical (the crystallization above 60° C. is less than 40%, Ec<0.4). It was discovered that only one of the PBE samples was able to match the 40% enthalpy of crystallization, however, as it will be shown below, this composition has unacceptable E2 value.

Compositions of POE and COC with matching transition temperatures in the 70° C. to 100° C. temperature range. In this case, the POE selected had a Tm peak of 82° C., and the COC a Tg of 77° C. Various levels of the COC where explored in the 3 to 15 wt % range. It has been discovered, as shown in the graph, these compositions preserve the crystallization behavior of the POE (EC≥0.4 and Tc peak ≥60° C.).

Dispersion

It has been discovered that that the following two temperature constraints can be used to optimize the dispersion of the polymer components of the film compositions. The two temperature dependent constraints are as follows: 1) a target temperature of 85° C., below which, it is desire the composition exhibits its DSC melting temperature peak (Tm), and 2) a target temperature of 95° C., below which, it is desire the composition exhibits its DSC onset Tm at end of melting. Above the “onset Tm, at end of melting,” the melting profile ends and returns to the DSC base line, and the composition is considered molten.

E1. Fraction of the enthalpy of melting below 85° C., relative to the total enthalpy of melting measured by DSC. See FIG. 5. E2. Fraction of the enthalpy of melting between Tm and 95° C., relative to the enthalpy of melting above Tm measured by DSC. See FIG. 6.

Based on the above analyses, it has been discovered that the three efficiencies (Ec, E1, E2) are required to approach one, to minimize processing time and eliminate the presence of undispersed polymer (gels) after compounding. FIG. 4-5 show a schematic of the efficiencies defined here. See also Tables 4 and 5 below.

TABLE 4 Index Equal to 1 (Preferred) Equal to 0 (Not preferred) Parameter Ec FAST SLOW Processing The composition fully crystallized The composition has not started time above 60° C. to crystallize at 60° C. E1 No gels in final product Gels in final product Dispersion The composition is in the molten The composition's crystallinity state past 85° C. is too high and it has not started to melt at 85° C. E2 No gels in final product Gels in final product Dispersion The bulk of the composition is in The compositions crystallinity is too the molten state near 85° C. and it high and has remaining crystallinity is in the molten state past 95° C. beyond 95° C.

TABLE 5 Stress Stress Tm Tm onset at @7% @25% peak, end of strain, ksi strain, ksi ° C. melting, ° C. E1 E2 Ec Comp. F1 EVA1 0.29 0.58 86 95 0.77 0.83 0.53 Comp. F2 EVA2 0.38 0.65 85 93 0.81 0.91 0.48 Comp. F3 EVA3 0.33 0.60 85 92 0.85 0.93 0.47 Comp. F4 POE1 0.25 0.47 84 93 0.87 0.97 0.43 Comp. F5 POE2 0.46 0.68 91 96 0.65 0.87 0.59 Comp. F6 POE3 0.45 0.72 93 101 0.55 0.36 0.62 Comp. F7 POE1 with 0.35 0.56 83 91 0.90 0.97 0.43 COC @3 wt % Inv. F1 POE1 with 0.57 0.76 83 92 0.90 0.96 0.43 COC @9 wt % Comp. F8 POE1 with 1.08 1.17 83 92 0.89 0.95 0.43 COC @15 wt % Inv. F2 POE1 with 0.65 0.81 83 94 0.86 0.94 0.42 COC @10 wt % Inv. F3 POE1 with 0.65 0.87 83 92 0.88 0.95 0.58 COC @10 wt % Comp. F9 POE1 with PBE 0.42 0.68 80 96 0.84 0.85 0.35 Comp. F10 POE1 with PBE 0.46 0.71 80 109 0.73 0.67 0.41 Comp. F11 POE1 with PBE 0.42 0.69 80 95 0.89 0.94 0.35 Comp. F12 POE1 with PBE 0.51 0.78 82 99 0.80 0.86 0.38 Inv. F4 POE1 with 0.58 0.80 83 92 0.89 0.96 0.43 COC @10 wt % Inv. F5 POE1 with 0.71 0.87 83 96 0.85 0.88 0.43 COC @10 wt % POE1 = ENGAGE 8003, POE2 = NORDEL IP 4820, POE3 = AFFINITY 1140, COC = TOPAS 8007F-04 (noted as “TOPAS 8007” in some tables), EVA1 = ELVAX 460, EVA2 = ELVAX 470, EVA3 = ALCUDIA 537, PBE = VERSIFY 2200.

TABLE 6 Processing Conditions, Multilayer Films Extruder 1 Extruder 2 Extruder 3 Extruder 4 Extruder 5 Barrel 1° C. 132 132 132 132 132 Barrel 2° C. 149 149 149 149 149 Barrel 3° C. 177 177 177 177 177 Barrel 4° C. 188 — — — 188 Die ° C. 216 216 216 216 216 Melt ° C. 209 216 219 21 211 Pressure 17.7 26.3 22.3 27.4 18.8 (MPa) Speed rpm 52 62 129 62 51 Current % 81 63 62 60 75 Production 3.6 1.9 3.5 1.9 3.6 rate kg/hr

TABLE 7A EVA1 (Comp. F1) EVA2 (Comp. F2) EVA3 (Comp. F3) Total Gauge 6 mil 6 Mil 6 mil Amt. wt % Component Amt. wt % Component Amt. wt % Component Layer 1 95 ELVAX 460 20 ELVAX 460 94 ALCUDIA 539 74 ELVAX 470 2.5 AMPACET 10090 2.5 AMPACET 3 AMPACET 3 AMPACET 100450 100329 100329 3 AMPACET 3 AMPACET 100342 100342 Total 100 100 100 Layer 2 100 ELVAX 460 20 ELVAX 460 100 ALCUDIA 537 80 ELVAX 470 Total 100 100 100 Layer 3 100 ELVAX 460 20 ELVAX 460 100 ALCUDIA 537 0 80 ELVAX 470 0 0 0 0 Total 100 100 100 Layer 4 100 ELVAX 460 20 ELVAX 460 100 ALCUDIA 537 0 80 ELVAX 470 0 Total 100 100 100 Layer 5 95 ELVAX 460 20 ELVAX 460 94 ALCUDIA 537 0 74 ELVAX 470 0 2.5 AMPACET 0 0 10090 2.5 AMPACET 3 AMPACET 3 AMPACET 100450 100329 100329 3 AMPACET 3 AMPACET 100342 100342 Total 100 100 100 Overall Amt. wt % Thickness mil Amt. wt % Thickness mil Amt. wt % Thickness mil Layer 1 30 1.8 30 1.8 30 1.8 Layer 2 10 0.6 10 0.6 10 0.6 Layer 3 20 1.2 20 1.2 30 1.8 Layer 4 10 0.6 10 0.6 10 0.6 Layer 5 30 1.8 30 1.8 20 1.2 Total 100 6 100 6 100 6 Die Size, in 2.95 2.95 2.95 Film Gauge, mil 6 6 6 Layflat, in width 11.6 11.6 14.0 BUR 2.5 2.5 3.0 Die gap, mil 78.7 78.7 78.7

TABLE 7B POE1 (Comp. F4) POE2 (Comp. F5) POE3 (Comp. F6) Total Gauge 6.5 Mil 6.5 Mil 6.5 mil Amt. wt % Component Amt. wt % Component Amt. wt % Component Layer 1 94 ENGAGE 8003 94 NIP4820 94 AFFINITY 1140 3 AMPACET 3 AMPACET 3 AMPACET 100329 100329 100329 3 AMPACET 3 AMPACET 3 AMPACET 100342 100342 100342 Total 100 100 100 Layer 2 100 ENGAGE 8003 100 NIP4820 100 AFFINITY 1140 Total 100 100 100 Layer 3 100 ENGAGE 8003 100 NIP4820 100 AFFINITY 1140 Total 100 100 100 Layer 4 100 ENGAGE 8003 100 NIP4820 100 AFFINITY 1140 Total 100 100 100 Layer 5 94 ENGAGE 8003 94 NIP4820 94 AFFINITY 1140 3 AMPACET 3 AMPACET 3 AMPACET 100329 100329 100329 3 AMPACET 3 AMPACET 3 AMPACET 100342 100342 100342 Total 100 100 100 Overall Amt. wt % Thickness mil Amt. wt % Thickness mil Amt. wt % Thickness mil Layer 1 25 1.625 20 1.3 30 1.95 Layer 2 15 0.975 15 0.975 10 0.65 Layer 3 20 1.3 30 1.95 20 1.3 Layer 4 15 0.975 15 0.975 10 0.65 Layer 5 25 1.625 20 1.3 30 1.95 Total 100 6.5 100 6.5 100 6.5 Die Size, in 2.95 2.95 2.95 Film Gauge, mil 6.5 6.5 6.5 Layflat, in width 14 14 14 BUR 3.0 3.0 3.0 Die gap, mil 78.7 78.7 78.7

TABLE 7C POE1 with COC @ 3 wt % POE1 with COC @ 9 wt % POE1 with COC @ 15 wt % (Comp. F7) (Inv. F1) (Comp. F8) Total Gauge 5.9 Mil 5.9 Mil 5.9 mil Amt. wt % Component Amt. wt % Component Amt. wt % Component Layer 1 91 ENGAGE 8003 85 ENGAGE 8003 79 ENGAGE 8003 3 TOPAS 8007 9 TOPAS 8007 15 TOPAS 8007 3 AMPACET 3 AMPACET 3 AMPACET 100329 100329 100329 3 AMPACET 3 AMPACET 3 AMPACET 100342 100342 100342 Total 100 100 100 Layer 2 97 Engage 8003 91 Engage 8003 85 Engage 8003 3 TOPAS 8007 9 TOPAS 8007 15 TOPAS 8007 Total 100 100 100 Layer 3 97 ENGAGE 8003 91 ENGAGE 8003 85 ENGAGE 8003 3 TOPAS 8007 9 TOPAS 8007 15 TOPAS 8007 Total 100 100 100 Layer 4 97 ENGAGE 8003 91 ENGAGE 8003 85 ENGAGE 8003 3 TOPAS 8007 9 TOPAS 8007 15 TOPAS 8007 Total 100 100 100 Layer 5 91 ENGAGE 8003 85 ENGAGE 8003 79 ENGAGE 8003 3 TOPAS 8007 9 TOPAS 8007 15 TOPAS 8007 3 AMPACET 3 AMPACET 3 AMPACET 100329 100329 100329 3 AMPACET 3 AMPACET 3 AMPACET 100342 100342 100342 Total 100 100 100 Overall Amt. wt % Thickness mil Amt. wt % Thickness mil Amt. wt % Thickness mil Layer 1 30 1.8 30 1.8 30 1.8 Layer 2 10 0.6 10 0.6 10 0.6 Layer 3 20 1.2 20 1.2 30 1.8 Layer 4 10 0.6 10 0.6 10 0.6 Layer 5 30 1.8 30 1.8 20 1.2 Total 100 5.9 100 5.9 100 5.9 Die Size, in 2.95 2.95 2.95 Film Gauge, mil 5.9 5.9 5.9 Layflat, in width 14 14 14 BUR 3.0 3.0 3.0 Die gap, mil 78.7 78.7 78.7

TABLE 7D POE1 with COC @ POE1 with PBE POE1 with PBE 10 wt % (Inv. F2) (Comp. F9) (Comp. F10) Total Gauge 6.5 mil 6 Mil 6 mil Amt. wt % Component Amt. wt % Component Amt. wt % Component Layer 1 84 ENGAGE 8003 90 AFFINITY 80 AFFINITY 8770 8770 10 TOPAS 8007 10 LDPE 1321 3 AMPACET 5 AMPACET 5 AMPACET 100329 10090 10090 3 AMPACET 5 AMPACET 5 AMPACET 100342 100450 100450 Total 100 100 100 Layer 2 90 ENGAGE 8003 100 AFFINITY 90 AFFINITY 8770 8770 10 TOPAS 8007 10 LDPE 1321 Total 100 100 100 Layer 3 90 ENGAGE 8003 100 VERSIFY 100 VERSIFY 2200 2200 10 TOPAS 8007 0 0 Total 100 100 100 Layer 4 90 ENGAGE 8003 100 AFFINITY 90 AFFINITY 8770 8770 10 TOPAS 8007 0 10 LDPE 1321 Total 100 100 100 Layer 5 84 ENGAGE 8003 90 AFFINITY 80 AFFINITY 8770 8770 10 TOPAS 8007 0 10 LDPE 1321 3 AMPACET 5 AMPACET 5 AMPACET 100329 10090 10090 3 AMPACET 5 AMPACET 5 AMPACET 100342 100450 100450 Total 100 100 100 Overall Amt. wt % Thickness mil Amt. wt % Thickness mil Amt. wt % Thickness mil Layer 1 30 1.95 20 1.2 20 1.2 Layer 2 10 0.65 15 0.9 15 0.9 Layer 3 20 1.3 30 1.8 30 1.8 Layer 4 10 0.65 15 0.9 15 0.9 Layer 5 30 1.95 20 1.2 20 1.2 Total 100 6.5 100 6 100 6 Die Size, in 2.95 2.95 2.95 Film Gauge, mil 6.5 6 6 Layflat, in width 14 14 14 BUR 3.0 3.0 3.0 Die gap, mil 78.7 78.7 78.7

TABLE 7E POE1 with PBE (Comp. F11) Total Gauge 6 Mil Layer 1 Amt. wt % Component 86 ENGAGE 8003 7 AMPACET 100329 7 AB Total 100 Layer 2 Amt. wt % Component 100 ENGAGE 8003 Total 100 Layer 3 Amt. wt % Component 100 VERSIFY 2200 Total 100 Layer 4 Amt. wt % Component 100 ENGAGE 8003 Total 100 Layer 5 Amt. wt % Component 86 ENGAGE 8003 7 AMPACET 100329 7 AB Total 100 Overall Amt. wt % Thickness mil Layer 1 20 1.2 Layer 2 15 0.9 Layer 3 30 1.8 Layer 4 15 0.9 Layer 5 20 1.2 Total 100 6 Die Size, in 2.95 Film Gauge, mil 6 Layflat, in width 14 BUR 3.0 Die gap, mil 78.7

TABLE 7F POE1 with COC @ 10% POE1 with COC @ (Inv. F4 (collapsed bubble) 10% (Inv. F5 Total Gauge 2.85 mil 5.7 mil Layer 1 Amt. Component Amt. Component (inner layer) wt % wt %   100% Engage 8003   85% ENGAGE 8003   10% TOPAS 8007    2% AB    3% AMPACET 10090 Total 100 100 Layer 2 Amt. Component Amt. Component wt % wt %   91% Engage 8003   85% ENGAGE 8003    9% TOPAS 8007   10% TOPAS 8007    2% AB    3% AMPACET 10090 Total 100 100 Layer 3 Amt. Component Amt. Component wt % wt %   91% ENGAGE 8003   100% ENGAGE 8003    9% TOPAS 8007 Total 100 100 Layer 4 Amt. Component Amt. Component wt % wt %   85% Engage 8003   85% ENGAGE 8003   10% TOPAS 8007   10% TOPAS 8007    2% AB    2% AB    3% AMPACET 10090    3% AMPACET 10090 Total 100 100 Layer 5 Amt. Component Amt. Component  wt %  wt %   85% Engage 8003   85% ENGAGE 8003   10% TOPAS 8007   10% TOPAS 8007    2% AB    2% AB    3% AMPACET 10090    3% AMPACET 10090 Total 100 100 Overall Amt. Thickness mil Amt. Thickness mil wt % wt % Layer 1  14% 0.40  30% 1.71 Layer 2  15% 0.43  13% 0.741 Layer 3  38% 1.08  14% 0.798 Layer 4  13% 0.37  13% 0.741 Layer 5  20% 0.57  30% 1.71 Total 100% 2.85 100% 5.7 Die Size, in 2.95 2.95 Film Gauge, 2.85 5.7 mil Layflat, in 14 14 width BUR 3.0 3.0 Die gap, 78.7 78.7 mil

TABLE 8 POE1 with COC @ POE1 with PBE Total 10 wt % (Inv. F3) (Comp. F12) Gauge 5.7 mil 6 mil Layer Amt. Component Amt. Component 1 wt % ENGAGE 8003 wt % ENGAGE 8003 84 AMPACET 86 AMPACET 100329 100329 3 AMPACET 7 AMPACET 100342 100342 3 TOPAS 8007 7 10 Total 100 100 Layer Amt. Component Amt. Component 2 wt % ENGAGE 8003 wt % ENGAGE 8003 90 TOPAS 8007 86 AMPACET 100329 10 7 AMPACET 100342 7 Total 100 100 Layer Amt. Component Amt. Component 3 wt % ENGAGE 8003 wt % VERSIFY 2200 90 TOPAS 8007 100 10 Total 100 100 Layer Amt. Component Amt. Component 4 wt % ENGAGE 8003 wt % VERSIFY 2200 90 TOPAS 8007 100 10 0 Total 100 100 Layer Amt. Component Amt. Component 5 wt % ENGAGE 8003 wt % VERSIFY 2200 90 TOPAS 8007 100 10 Total 100 100 Layer Amt. Component Amt. Component 6 wt % ENGAGE 8003 wt % ENGAGE 8003 90 TOPAS 8007 86 AMPACET 100329 10 7 AMPACET 100342 7 Total 100 100 Layer Amt. Component Amt. Component 7 wt % ENGAGE 8003 wt % ENGAGE 8003 84 AMPACET 86 AMPACET 100329 100329 3 AMPACET 7 AMPACET 100342 100342 3 TOPAS 8007 7 10 Total 100 100

TABLE 9 POE1 with COC @ 10 wt % (Inv. F3) POE1 with PBE (Comp. F12) Amt. Thickness Amt. Thickness Overall wt % mil wt % mil Layer 1 15 0.855 15 0.9 Layer 2 15 0.855 20 1.2 Layer 3 15 0.855 10 0.6 Layer 4 10 0.57 10 0.6 Layer 5 15 0.855 10 0.6 Layer 6 15 0.855 20 1.2 Layer 7 15 0.855 15 0.9 Total 100 5.7 100 6 Operation Instructions Die Size, in 9.84 9.84 Film Gauge, mil 5.7 6 BUR 3.5 3.5 Layflat, in width 54.1 54.1 Net Layflat, in 54 54 Die gap, mil 78.7 78.7

Summary of Results

Complete mixing in the case of polymeric components in such formulations has been correlated with the high flowability, which results after a material transition, such as melting or glass transition. New compositions have been developed that fulfill a series of temperature dependent constraints, to provide good flowability and high stiffness at ambient temperatures, for adequate transportation of the bagged material. The good flowability allows for ready dispersion of the composition at temperatures in the range from 90° C. to 150° C., and for high hot tack, at sealing temperatures, during packaging operations (>100° C.).

It has been discovered that compositions containing an ethylene-based polymer and a cycloolefin interpolymer that have overlapping transition temperatures in the 70-100 C range have excellent processing properties, dispersion properties and tensile properties, and can be used to form films with excellent physical properties. The inventive compositions have good flowability and therefore good mixing of a final film formulation.

It has also been discovered that such compositions provides an optimization of the tensile properties, as well as processing time. The processing time is the time required for the composition to cool below its transition temperature, and therefore recover the typical properties of a solid-like material. In the case of olefin-based polymers, crystallinity is typically varied to tailor melting behavior, tensile properties, and processing time, however, the inventive compositions do not completely rely on crystallinity to have superior physical properties. For example, both tensile properties and fast processing time benefit from maximizing crystallinity, while good dispersion and fast mixing benefit from low crystallinity. It has been discovered that the inventive compositions have an optimal balance of the ethylene-based polymer (POE) and the cycloolefin interpolymer (COC) to provide an optimal balance between flowability and modulus.

TABLE 10A EVA1 EVA2 EVA3 POE1 POE2 POE3 Comp. Comp. Comp. Comp. Comp. Comp. F1 F2 F3 F4 F5 F6 Average Density — 0.9408 0.9397 0.9396 0.8878 0.9102 0.8998 Average Flow Units vary 2.8 1.4 1.0 0.9 1.0 1.7 Rate, I2 @190 C. Puncture Avg-Break Load lbf 28 32 35 14 15 13 Avg-Elongation in 5.7 5.4 5.9 4.2 3.3 3.5 At Break Avg-Energy To in*lbf 102 108 124 55 47 49 Break Avg-Peak Load lbf 29 32 35 21 21 21 Avg-Puncture ft*lbf/in{circumflex over ( )}3 111 116 136 56 48 50 Secant Avg-Modulus psi 6572 6206 6027 4189 8393 7158 Modulus - Avg-Secant psi 6283 6240 6043 4213 8425 7176 CD Modulus At 1% Avg-Secant psi 5978 6170 5932 4165 8306 7093 Modulus At 2% Secant Avg-Modulus psi 6622 6264 5630 60898 8162 7545 Modulus - Avg-Secant psi 6404 6293 5661 3978 8280 7498 MD Modulus At 1% Avg-Secant psi 6063 6203 5593 4040 8099 7407 Modulus At 2% Tensile - Avg-Break Stress psi 2538 1082 979 4497 1073 1095 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 874 260 235 785 253 282 CD Volume At Break Avg-Energy To in*lbf 124 39 37 127 41 43 Break Avg-Peak Load lbf 15 7 6 30 7 7 Avg-Strain At % 830 369 363 680 335 367 Break Avg-Strain At % 24 19 20 18 16 19 Yield Avg-Stress At psi 562 595 540 425 624 662 Yield Tensile - Avg-Break Stress psi 3186 1074 1102 4085 1123 1072 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 1055 224 252 725 259 262 MD Volume At Break Avg-Energy To in*lbf 148 31 37 111 41 42 Break Avg-Peak Load lbf 18 6 7 26 8 7 Avg-Strain At % 869 307 351 633 329 342 Break Avg-Strain At % 20 19 20 20 17 19 Yield Avg-Stress At psi 539 609 560 445 654 668 Yield Avg VICAT C.- 61 65 65 69 81 79 Thickness mil 6.0 6.0 6.2 6.4 6.5 6.5

TABLE 10B POE1 POE1 POE1 POE1 POE1 with with with with with COC @3% COC @9% COC @15% COC @10% COC @10% Result Units Comp. F7 Inv. F1 Comp. F8 Inv. F2 Inv. F3 Average Density — — — — 0.8983 0.8998 Average Flow Rate, Units vary — — — 0.9 0.9 I2 @190 C. Puncture Avg-Break Load lbf 15 15 22 19 26 Avg-Elongation at in 4.4 3.8 3.1 3.5 3.8 Break Avg-Energy To in*lbf 58 55 42 58 57 Break Avg-Peak Load lbf 22 24 22 26 26 Avg-Puncture ft*lbf/in{circumflex over ( )}3 67 63 56 58 67 Secant Avg-Modulus psi — — — 9720 6435 Modulus - Avg-Secant psi — — — 9743 6489 CD Modulus At 1% Avg-Secant psi — — — 9427 6383 Modulus At 2% Secant Avg-Modulus psi — — — 13786 17209 Modulus - Avg-Secant psi — — — 13778 17147 MD Modulus At 1% Avg-Secant psi — — — 13337 16516 Modulus At 2% Tensile - Avg-Break Stress psi 5219 4554 4237 1118 1122 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 983 958 1029 209 194 CD Volume At Break Avg-Energy To in*lbf 136 133 133 32 26 Break Avg-Peak Load lbf 30 26 23 7 6 Avg-Strain At Break % 697 646 584 284 267 Avg-Strain At Yield % 18 19 22 17 27 Avg-Stress At Yield psi 496 643 890 638 692 Tensile - Avg-Break Stress psi 4863 4075 3151 1203 1206 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 988 888 688 183 133 MD Volume At Break Avg-Energy To in*lbf 142 122 113 30 18 Break Avg-Peak Load lbf 29 23 22 8 7 Avg-Strain At Break % 693 592 444 228 159 Avg-Strain At Yield % 20 16 8 10 12 Avg-Stress At Yield psi 519 701 1074 670 751 Avg VICAT C.- 65 72 71 72 67 Thickness mil 5.9 5.8 5.8 6.5 5.6

TABLE 10C POE1 POE1 POE1 POE1 with PBE with PBE with PBE with PBE Comp. Comp. Comp. Result Units Comp. F9 F10 F11 F12 Average Density — — — 0.8882 0.8901 Average Flow Rate, Units vary — — 0.9 1.1 I2 @190 C. Puncture Avg-Break Load lbf 13 14 17 10 Avg-Elongation At in 4.8 3.9 1.3 2.2 Break Avg-Energy To in*lbf 64 45 38 16 Break Avg-Peak Load lbf 22 19 17 11 Avg-Puncture ft*lbf/in{circumflex over ( )}3 71 46 44 18 Secant Avg-Modulus psi 7387 7984 8020 7810 Modulus - Avg-Secant Modulus psi 7389 8005 8044 7802 CD At 1% Avg-Secant Modulus psi 7272 7866 7934 7625 At 2% Secant Avg-Modulus psi 7822 8405 7097 7913 Modulus - Avg-Secant Modulus psi 7811 8436 7209 7998 MD At 1% Avg-Secant Modulus psi 7658 8274 7073 7769 At 2% Tensile - Avg-Break Stress psi 4381 3841 1329 4838 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 846 1223 1015 894 CD Volume At Break Avg-Energy To in*lbf 132 183 141 124 Break Avg-Peak Load lbf 29 26 12 28 Avg-Strain At Break % 701 812 912 628 Avg-Strain At Yield % 101 710 623 16 Avg-Stress At Yield psi 707 3940 2012 721 Tensile - Avg-Break Stress psi 4935 5121 1241 4255 Film - Avg-Energy Per ft*lbf/in{circumflex over ( )}3 901 1107 1063 1166 MD Volume At Break Avg-Energy To in*lbf 131 153 149 158 Break Avg-Peak Load lbf 30 28 12 25 Avg-Strain At Break % 693 751 912 763 Avg-Strain At Yield % 101 747 593 16 Avg-Stress At Yield psi 737 4840 1991 724 Avg VICAT C.- — — 67 64 Thickness mil 6.2 6.3 5.9 5.7

TABLE 10D POE1 with COC POE1 with COC @ 10% (Inv. F4) @ 10% (Inv. F5) Result Units Average Density — 0.8962 0.8984 Average Flow Rate, Units vary 1.0 1.0 12 @ 190 C Puncture Avg-Break Load lbf 24 24 Avg-Elongation At Break in 4.5 4.2 Avg-Energy To Break in*lbf 72 69 Avg-Peak Load lbf 26 27 Avg-Puncture ft*lbf/in{circumflex over ( )}3 86 82 Tensile- Avg-Break Stress psi 4557 4341 Film-CD Avg-Energy Per ft*lbf/in{circumflex over ( )}3 845 864 Volume At Break Avg-Energy To Break in*lbf 119 116 Avg-Peak Load lbf 27 24 Avg-Strain At Break % 595 578 Avg-Strain At Yield % 19 19 Avg-Stress At Yield psi 686 741 Tensile - Avg-Break Stress psi 4910 4047 Film -MD Avg-Energy Per ft*lbf/in{circumflex over ( )}3 1032 880 Volume At Break Avg-Energy To Break in*lbf 134 126 Avg-Peak Load lbf 27 24 Avg-Strain At Break % 594 557 Avg-Strain At Yield % 17 18 Avg-Stress At Yield psi 765 837 Avg VICAT C- 63 63 Thickness mil 5.9 5.6 

What is claimed is:
 1. A composition comprising at least the following components: A) an ethylene-based polymer; B) a cycloolefin interpolymer comprising, in polymerized form, ethylene and at least one bridged cyclic olefin selected from the following: a)

Structure a, wherein R1 and R2 are each, independently, selected from hydrogen, an alkyl; b)

Structure b, wherein R3 and R4 are each, independently, selected from hydrogen, an alkyl; c)

Structure c, wherein R5 and R6 are each, independently, selected from hydrogen, an alkyl; d)

Structure d, wherein R7 and R8 are each, independently, selected from hydrogen, an alkyl; e) or any combination of a) through d); and wherein component A is present in an amount ≥50 wt %, based on the weight of the composition, and wherein component B is present in an amount from 5 to 12 wt %, based on the sum weight of components A and B.
 2. The composition of claim 1, wherein the cycloolefin interpolymer of component B has a Tg from 60° C. to 90° C.
 3. The composition of claim 1, wherein the ethylene-based polymer of component A has a Tm from 80° C. to 95° C.
 4. The composition of claim 1, where the ethylene-based polymer of component A has a density ≤0.900 g/cc.
 5. The composition of claim 1, wherein the weight ratio of component A to component B is from 4.0 to 20.0.
 6. The composition of claim 1, wherein the ethylene-based polymer of component A is an ethylene/α-olefin copolymer.
 7. The composition of claim 1, wherein the cycloolefin interpolymer is an ethylene/bridged cyclic olefin copolymer.
 8. The composition of claim 1, the composition comprising ≥80 wt % of component A, ≥9 wt % of component B, and ≥5 wt % of an additive.
 9. A film comprising at least one layer formed from the composition of claim
 1. 10. The film of claim 9, and wherein the film comprises at least one additional layer, formed from a composition that comprises from 1 to 12 wt % of an ethylene/bridged cyclic olefin interpolymer, based on the weight of this composition.
 11. An article comprising at least one component formed from the composition of claim
 1. 